4130H hardened heavy alloy steel plate
4130H TOOL STEEL (Holderblock) is a prehardened CrMnMo S-alloyed
tool steel for the construction of plastic molds.
4130H TOOL STEEL is applied by the customers for accessories with
such holderblock requirements as ejector plates, supports, clamping
plates and housings for diecasting dies. It is characterized by
excellent dimensional stability as well as good machinability. It
is also suitable for molds with low surface requirements referring
to polishability.
Product description
Designation and range of application
4130H TOOL STEEL is a modified version of AISI 4130 in holderblock
quality.
4130H TOOL STEEL is available as plate with flame cut edges in the
following dimensions:
| Thickness | > 12 ≤ 200 mm | > 1/2 ≤ 7 3/4 inch |
| Width | ≥ 1250 ≤ 2500 mm | ≥ 49 ≤ 98 inch |
| Length | ≥ 4000 ≤ 6000 mm | ≥ 157 1/2≤ 236 inch |
Other dimensions available upon request.
Production
The 4130H TOOL STEEL production route is designed to achieve the
excellent machinability and dimensional stability of this
holderblock steel type. The good oxidic cleanliness, the large
number of sulfides and the modification of the few remaining
inclusions by the calcium treatment lead to good machinability,
high dimensional stability and minimize the tool wear. 4130H TOOL
STEEL should only be applied for molds if the surface requirements
are low referring to polishability. 4130H TOOL STEEL should not be
applied for photoetching and spark erosion.
These properties can only be achieved by the combination of the
following 4130H TOOL STEEL-production steps:
· chemical analysis in dependence of dimensions
· vacuum degassing
· argon stirring for high sulfidic and oxidic cleanliness
· suplphur alloying
· calcium treatment for inclusion shape control
· special casting conditions to assure the high cleanliness and
homogenity
· High Shape Factor Rolling (high thickness reduction) to realize a
closely packed structure
· appropriate heat treatment parameters according to analysis and
dimensions to assure homogeneous hardness distribution over the
plate and to minimize residual stresses
Chemical composition
For the ladle analysis the following limiting values in % are
applicable
| C | Si | Mn | P | S | Cr | Mo | V |
| 0.28-0.35 | 0.15-0.40 | 0.95-1.30 | ≤0.030 | 0.010-0.040 | 0.60-0.90 | 0.15-0.25 | ≥0.02 |
Delivery condition
4130H TOOL STEEL is supplied in the prehardened (water quenched +
tempered) condition.
Mechanical and technological properties in the delivery condition
Hardness
Unless otherwise agreed the hardness at the surface in the delivery
condition is 265 - 310 HB. According to EN 18265, table B2, this
corresponds to a tensile strength of approximately 840 - 985 MPa
(121 - 142 ksi).
Testing
· Heat analysis
· Dimension control
· Surface inspection
· Hardness
The hardness (HB) is tested on surface of each rolled mother plate.
· Ultrasonic testing
Unless otherwise agreed, 100 % ultrasonic testing is performed on
each plate in the delivery condition in accordance with ASTM A 578,
Level B.
Upon request, an ultrasonic testing in accordance with EN 10160 is
possible. As admissible limit apply quality class 3 for thicknesses
£ 150 mm (6 in) and quality class 2 in table 5 of EN 10228-3 for
thicknesses > 150 mm (6 in). In this case the desired testing
type has to be indicatd on the order.
Unless otherwise agreed, the results are documented in an
inspection certificate 3.1 in accordance with EN 10204.
Identification of plates
Unless otherwise agreed the marking is carried out via steel stamps
with at least the following information:
· steel grade (4130H TOOL STEEL)
· heat number
· number of mother plate and individual plate
· the manufacturer’s symbol
· inspector’s sign
Processing
Heat treatment
4130H TOOL STEEL is delivered in the prehardened condition;
therefore further heat treatment is generally not necessary. This
avoids the risks and costs involved by the hardening and tempering
of a mold after processing. Should a heat treatment become
necessary, the following data are recommended:
| soft annealing | stress relieving | Preheating before hardening | hardening | tempering |
700 - 720 °C (1290 - 1330 °F) 2 - 4 h, furnace cooling hardness about 230 HB | in the delivery condition max. 600 °C (1110 °F) 1 - 2 h, furnace cooling
| 450 - 650 °C (840 - 1200 °F)
| 840 - 860 °C (1540 - 1580 °F)/oil; for low wall thicknesses warm
bath hardening at 200 - 230 °C (390 - 450 °F) is possible | in accordance with tempering diagram to required hardness (min. 1
h/25 mm (1 in) wall thickness) |
General technical delivery requirements
Unless otherwise agreed, the general technical delivery
requirements in accordance with EN 10021 apply.
Tolerances
Unless otherwise agreed, tolerances are in accordance with EN 10029
/ ASTM A 6 with the following restrictions:
| plate thickness: | in accordance with EN 10029, class C / ASTM A 6 |
| plate width: | ≥1250 mm≤1500 mm | ± 25 mm | ≥49≤59 in | ± 1 in |
| >1500 mm≤2000 mm | ± 40 mm | >59≤79 in | ± 1 1/2 in |
| >2000 mm | ± 50 mm | >79 in | ± 2 in |
| plate length: | | ± 1000 mm | | ± 40 in |
| flatness: | ≤3 mm/m |
Unless otherwise agreed, short lengths ≥2 m (79 in) are part of the
delivery.
Surface quality
Unless otherwise agreed, the specifications will be in accordance
with EN 10163-2 class A, subclass 3. Shot blasting of upper and
lower surface of the plate and shop priming are possible on
request.
General note
If special requirements, which are not listed in this
specification, are to be met by the steel due to its intended use
or processing, these requirements are to be agreed before placing
the order.
The information in this specification is a product description.
This specification is updated if necessary. The latest version is
available from the mill.
Production process